Arlon R37480X008 0.008" (0.203 mm) Uncured Silicone Rubber with Substrate: PTFE Coated Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R37480X008 0.008" (0.203 mm) Uncured Silicone Rubber with Substrate: PTFE Coated Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Primerless Thermabond® electrically insulating, thermally conductive, electronic adhesive. Bonds without primer.Design/Construction: Liner: FEP Add-on: Uncured Silicone Rubber Substrate: PTFE Coated Fiberglass Product Use: Electrically insulating electronic adhesive. Bonds without primer.Appearance: Gray, high viscosity gum on fluoropolymer release linersThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.80 g/cc | 0.101 lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| Thickness | 25.4 microns | 1.00 mil | Liner |
| 76.2 microns | 3.00 mil | Carrier | |
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | Silicone Property; ASTM D2240 |
| Tensile Strength | 4.72 MPa | 685 psi | Silicone Property; ASTM D412 |
| Tensile Strength, Yield | 24.5 MPa @Strain <=1.00 % |
3550 psi @Strain <=1.00 % |
Silicone Property; ASTM E 831 |
| Elongation at Break | 125 % | 125 % | Silicone Property; ASTM D412 |
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property |
| Shear Modulus | 0.00100 GPa @Strain <=25.0 % |
0.145 ksi @Strain <=25.0 % |
ASTM D 1002 |
| Shear Strength | 3.45 MPa | 500 psi | Arlon SQA-TMS-018 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 160 °C |
6.11 µin/in-°F @Temperature 68.0 - 320 °F |
Silicone Property; ASTM E 831 |
| Specific Heat Capacity | 0.820 J/g-°C @Temperature 100 °C |
0.196 BTU/lb-°F @Temperature 212 °F |
Silicone Property; Arlon SQA-TMS-052 |
| Thermal Conductivity | 1.40 W/m-K @Temperature 100 °C |
9.72 BTU-in/hr-ft²-°F @Temperature 212 °F |
Silicone Property; Arlon SQA-TMS-022 |
| Maximum Service Temperature, Air | 204.0 °C | 399.2 °F | |
| Minimum Service Temperature, Air | -136 °C | -212 °F | |
| Glass Transition Temp, Tg | -118 °C | -180 °F | Silicone Property; ASTM D3418 |
| Flammability, UL94 | V-0 | V-0 | Not Recognized |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 6.91 @Frequency 1.00e+6 Hz |
6.91 @Frequency 1.00e+6 Hz |
D<sub>k</sub>, Silicone Property; IPC TM 650 - 2.5.5.3 |
| Dielectric Strength | 31.5 kV/mm | 800 kV/in | ASTM D149 |
| Dissipation Factor | 0.0044 @Frequency 1.00e+6 Hz |
0.0044 @Frequency 1.00e+6 Hz |
D<sub>f</sub>, Silicone Property; IPC TM 650 - 2.5.5.3 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 121 °C |
0.250 hour @Temperature 250 °F |
After product reaches cure temperature, Recommended Cure Cycle |
| Shelf Life | 6.00 Month @Temperature 4.00 - 10.0 °C |
6.00 Month @Temperature 39.2 - 50.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Gray | |
| Total Product Weight (g/m2) | 479 | Arlon SQA-TMS-025 |