Arlon R37223N008 0.008" (0.203 mm) Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R37223N008 0.008" (0.203 mm) Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Side 1: Cured Silicone Rubber Substrate: Style 1653 Heat Cleaned Fiberglass ScrimSide 2: Cured Silicone RubberFiberglass Scrim Weave: LenoThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	25.4 microns	1.00 mil	Side 1; Arlon SQA-TMS-003
	25.4 microns	1.00 mil	Side 2; Arlon SQA-TMS-003
	152 microns	6.00 mil	Substrate; Arlon SQA-TMS-003
	203 microns	8.00 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60	60	Silicone Property; ASTM D2240
Tensile Strength	8.96 MPa	1300 psi	Silicone Property; ASTM D412
Elongation at Break	700 %	700 %	Silicone Property; ASTM D412
Tear Strength	43.8 kN/m	250 pli	Die B, Silicone Property; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
Shelf Life	12.0 Month @Temperature 23.9 °C	12.0 Month @Temperature 75.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Carmel Brown	Substrate
	Translucent	Silicone
Total Product Weight (oz/yd2)	1.6	Arlon SQA-TMS-025
Uncoated Fabric Break Strength	40 lb/in	Warp Strength, Arlon SQA-TMS-026
	43 lb/in	Fill Strength, Arlon SQA-TMS-026