Arlon R35551X014 0.014" (0.356 mm) Uncured Rubber with Coated Nextel Substrate (discontinued **)

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R35551X014 0.014" (0.356 mm) Uncured Rubber with Coated Nextel Substrate (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Uncured RubberSide 2: Uncured RubberSubstrate: Coated Nextel This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	76.2 microns	3.00 mil	Side 1; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Side 2; Arlon SQA-TMS-003
	203 microns	8.00 mil	Substrate; Arlon SQA-TMS-003
	356 microns	14.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40 - 50	40 - 50	Silicone Property; ASTM D2240
Tensile Strength	>= 5.52 MPa	>= 800 psi	Silicone Property; ASTM D412
Elongation at Break	>= 500 %	>= 500 %	Silicone Property; ASTM D412

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability, UL94	HB	HB	Compound Rated

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 121 - 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 250 - 350 °F	Recommended Cure Cycle

Descriptive Properties	Value	Comments
Color	Gray