Arlon R35121R063 0.063" (1.60 mm) Uncured Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon R35121R063 0.063" (1.60 mm) Uncured Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Uncured RubberSide 2: Uncured Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 76.2 microns
3.00 mil
Polyethylene, Interleave
483 microns
19.0 mil
Prime Coated 7500 Fiberglass, Substrate
533 microns
21.0 mil
Side 2
>= 584 microns
>= 23.0 mil
Side 1
1470 - 1730 microns
58.0 - 68.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 48 - 58
48 - 58
Compound Property, Side 1
52 - 62
52 - 62
Compound Property, Side 2
Tensile Strength >= 0.689 MPa
>= 100 psi
Compound Property, Side 2
>= 5.86 MPa
>= 850 psi
Compound Property, Side 1
Elongation at Break >= 300 %
>= 300 %
Compound Property, Side 1
>= 500 %
>= 500 %
Compound Property, Side 2
Peel Strength >= 1.40 kN/m
>= 8.00 pli
Bond Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
15.0 min

@Pressure 0.689 MPa,
Temperature 152 °C
0.250 hour

@Pressure 100 psi,
Temperature 305 °F
Recommended Cure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 53.2 - 62.6
Uncoated Fabric Break Strength 250 lb/in
Fill Direction, Substrate Property
300 lb/in
Warp Direction, Substrate Property