Arlon R34260N005 0.005" (0.127 mm) Unsupported/Uncured Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R34260N005 0.005" (0.127 mm) Unsupported/Uncured Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Unsupported/Uncured Rubber Appearance: Clear gum on release linersThis data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	25.4 microns	1.00 mil	FEP, Interleave
	76.2 microns	3.00 mil	PTFE Coated Fiberglass, Substrate
	102 - 152 microns	4.00 - 6.00 mil	Overall
	102 - 152 microns	4.00 - 6.00 mil	Side 1

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	35 - 45	35 - 45	Compound Property
Tensile Strength	>= 6.89 MPa	>= 1000 psi	Compound Property
Elongation at Break	>= 600 %	>= 600 %	Compound Property

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 138 °C	0.250 hour @Temperature 280 °F	Recommended Cure Cycle
Shelf Life	3.00 Month @Temperature 1.67 - 7.22 °C	3.00 Month @Temperature 35.0 - 45.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Natural
Total Product Weight (oz/yd2)	5.7 - 7.7