Arlon R33706R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R33706R026 0.026" (0.660 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Cured Silicone Rubber Side 2: Uncured Silicone Rubber Product Use: Flexible heater insulationAppearance: Red silicone gum and rubber on fiberglass with polymer release linersThis data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene, Interleave |
| 102 microns | 4.00 mil | Side 1 | |
| >= 178 microns | >= 7.00 mil | Side 2 | |
| 381 microns | 15.0 mil | Prime Coated 11523 Fiberglass, Substrate | |
| 610 - 711 microns | 24.0 - 28.0 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property |
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property |
| Elongation at Break | >= 500 % | >= 500 % | Compound Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 25.8 - 28.8 | |
| Uncoated Fabric Break Strength | 300 lb/in | Fill Direction, Substrate Property |
| 450 lb/in | Warp Direction, Substrate Property |