Arlon R33670N004 0.004" (0.102 mm) Uncured Silicone Rubber with K2030 PEN Film Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R33670N004 0.004" (0.102 mm) Uncured Silicone Rubber with K2030 PEN Film Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 25.4 microns | 1.00 mil | Interleave: Release liner to be determined (Temporarily FEP Film) |
| 50.8 microns | 2.00 mil | K2030 PEN Film, Substrate | |
| 25.4 - 76.2 microns | 1.00 - 3.00 mil | Side 1 | |
| 76.2 - 127 microns | 3.00 - 5.00 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property |
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property |
| Elongation at Break | >= 600 % | >= 600 % | Compound Property |
| Peel Strength | >= 0.351 kN/m | >= 2.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 160 °C | 320 °F | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 5.00 min @Pressure 0.345 MPa, Temperature 138 °C |
0.0833 hour @Pressure 50.0 psi, Temperature 280 °F |
Recommended Cure Cycle |
| Shelf Life | 3.00 Month @Temperature 4.44 °C |
3.00 Month @Temperature 40.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Total Product Weight (oz/yd2) | 3 - 4.8 | |
| Uncoated Fabric Break Strength | 31900 lb/in | Warp Direction, Substrate Property |
| 31900 lb/in | Fill Direction, Substrate Property |
Users viewing this material also viewed the following:
- Mallard Creek Polymers Rovene® 6102 Resin Supported Emulsion
- Indium Corp. Indalloy 86 Bismuth-Cadmium Solder Alloy
- MetalTek MTEK 317 Cast UNS J93000 Austenitic Stainless Steel
- Lucent Polymers GPB-130L Polybutylene Terephthalate, 30% Glass Fiber Reinforced
- Momentive Performance Materials SS4155 Silicone Primer for use with RTV Silicone Adhesive Sealants, Blue
- Techmer ES HiFill® PEI GF20 20% Glass Filled
- Universal Wire Works 505 E8018-B8 Stainless Steel Electrode
- Wingate Alloys Tuf-Last UV Resistant PE
- A. Schulman COMTUF® 462 Glass/Fiber Mineral Reinforced, Impact Modified PET Alloy
- Zircar Ceramics Z-MAG-B Non-RCF Blanket
Copyright © lookpolymers.com All Rights Reserved