- Arlon R31031R025 0.025" Uncured Silicone Rubber with Fiberglass Substrate
Arlon R31031R025 0.025" Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon R31031R025 0.025" Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Prime Coated 1564 FiberglassSide 2: Uncured Silicone RubberThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 127 microns | 5.00 mil | Side 1 |
| 127 microns | 5.00 mil | Side 2 | |
| 381 microns | 15.0 mil | Substrate | |
| 635 microns | 25.0 mil | Overall thickness |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | Silicone Property |
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Silicone Property |
| Elongation at Break | >= 300 % | >= 300 % | Silicone Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| Flammability Test | 3.0 | 3.0 | Char Length, inches; FTMS 191A; Method 5903 |
| 25 | 25 | Flame and Glow Time, seconds; FTMS 191A; Method 5903 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 32 | |
| Uncoated Fabric Break Strength (lb/in) | 350 | Fill Direction |
| 400 | Warp Direction |