Arlon P29609R015 0.015" (0.381 mm) Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon P29609R015 0.015" (0.381 mm) Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Layer-on-Layer Product Use: Traction motor insulation, electrical insulationAppearance: Red silicone gum on fiberglass clothThis data Represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 38.1 microns
1.50 mil
Polyethylene, Interleave
50.8 microns
2.00 mil
Side 1, Side 2, Uncured
127 microns
5.00 mil
Side 1, Side 1, Fully Cured
203 microns
8.00 mil
Prime Coated 7628 Fiberglass, Substrate
356 - 406 microns
14.0 - 16.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Compound Property
Tensile Strength >= 6.21 MPa
>= 900 psi
Compound Property
Elongation at Break >= 200 %
>= 200 %
Compound Property
Peel Strength >= 0.877 kN/m
>= 5.00 pli
Bond Strength
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 260 °C
500 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability Test <= 3.0
<= 3.0
[in], Char Length; FTMS 191A; Method 5903
<= 15
<= 15
[sec], Flame & Glow Time; FTMS 191A; Method 5903
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 177 °C
0.250 hour

@Temperature 350 °F
Recommended Cure Cycle
120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 6.00 Month

@Temperature 23.9 °C
6.00 Month

@Temperature 75.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 15.2 - 18.2
Uncoated Fabric Break Strength 200 lb/in
Fill Direction, Substrate Property
250 lb/in
Warp Direction, Substrate Property