Arlon 99790N010 0.010" (0.254 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 99790N010 0.010" (0.254 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Liner: FEP Side 1: Uncured Silicone Rubber Carrier: PTFE Coated FiberglassThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	25.4 microns	1.00 mil	Liner
	76.2 microns	3.00 mil	Carrier
	254 microns	10.0 mil	Side 1
	254 microns	10.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40	40	Silicone Property; ASTM D2240
Tensile Strength	8.96 MPa	1300 psi	Silicone Property; ASTM D412
Elongation at Break	770 %	770 %	Silicone Property; ASTM D412
Tear Strength	28.0 kN/m	160 pli	[ppiw], Die B, Silicone Property; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	36.0 Month @Temperature 7.22 °C	36.0 Month @Temperature 45.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Naturally Translucent
Total Product Weight (oz/yd2)	8.3	Arlon SQA-TMS-025

Users viewing this material also viewed the following: