Arlon 91B32R016AC Aluminum Clad Silicone Press Pad with "C-finish"

Category Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 91B32R016AC Aluminum Clad Silicone Press Pad with "C-finish".pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 2: Alloy 1100 H18 Aluminum FoilSide 1: Cured Silicone RubberThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
Silicone Property; Arlon SQA-TMS-024
2.70 g/cc
0.0975 lb/in³
Alloy 1100 Property (Annealed)
Thickness 102 microns
4.00 mil
Laminated Aluminum Foil; Arlon SQA-TMS-003
305 microns
12.0 mil
Silicone; Arlon SQA-TMS-003
406 microns
16.0 mil
Overall Thickness; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Tensile Strength 10.21 MPa
1481 psi
Silicone Property; Arlon SQA-TMS-008
165 MPa
23900 psi
Alloy 1100 Property; ASTM D345
Tensile Strength, Yield 145 MPa
21000 psi
Alloy 1100 Property; ASTM E345
Elongation at Break 263 %
263 %
Silicone Property; Arlon SQA-TMS-008
Peel Strength 1.77 kN/m
10.1 pli
Silicone Compound Property - Adhesion Strength to Aluminum; Arlon SQA-TMS-011
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 100 - 300 °C

@Pressure 0.000 - 10.0 MPa
212 - 572 °F

@Pressure 0.000 - 1450 psi
Component Elements Properties Metric English Comments
Aluminum, Al >= 99 %
>= 99 %
Alloy 1100
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature 21.1 °C
12.0 Month

@Temperature 70.0 °F
Descriptive Properties Value Comments
Rigidity (grams) 8500
Arlon Gurley Test; Alloy 1100 Property
Temper H18
Total Product Weight (oz/yd2) 19.5
Arlon SQA-TMS-025