Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 55578R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction: Interleave: LDPESide 2, Layer 2: Uncured Silicone Rubber Side 2, Layer 1: Cured Silicone Rubber Substrate: Style 162 Fiberglass Side 1: Silicone Skim Coat Appearance: Red silicone gum and/or rubber on fiberglass clothThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Side 2, Layer 2; Compound Property; Arlon SQA-TMS-024
1.35 g/cc
0.0488 lb/in³
Side 1 and Side 2, Layer 1; Compound Property; Arlon SQA-TMS-024
Thickness 38.1 microns
1.50 mil
Side 1; Arlon SQA-TMS-003
63.5 microns
2.50 mil
Interleave
76.2 microns
3.00 mil
Side 2, Layer 1; Arlon SQA-TMS-003
191 microns
7.50 mil
Side 2, Layer 2; Arlon SQA-TMS-003
406 microns
16.0 mil
Substrate; Arlon SQA-TMS-003
711 microns
28.0 mil
Overall; Arlon SQA-TMS-003
Mechanical Properties Metric English Comments
Hardness, Shore A 44
44
Side 2, Layer 2; Compound Property; ASTM D2240
52
52
Side 1 and Side 2, Layer 1; Compound Property; ASTM D2240
Tensile Strength 6.14 MPa
890 psi
Side 1 and Side 2, Layer 1; Compound Property; ASTM D412
7.58 MPa
1100 psi
Side 2, Layer 2; Compound Property; ASTM D412
Elongation at Break 550 %
550 %
Side 1 and Side 2, Layer 1; Compound Property; ASTM D412
650 %
650 %
Side 2, Layer 2; Compound Property; ASTM D412
Peel Strength 3.86 kN/m
22.0 pli
Bond Strength; ASTM D624
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
UL RTI, Electrical 220 °C
428 °F
E54153
UL RTI, Mechanical without Impact 200 °C
392 °F
E54153
Electrical Properties Metric English Comments
Dielectric Strength 19.3 kV/mm
489 kV/in
ASTM D149
Processing Properties Metric English Comments
Cure Time 15.0 min

@Temperature 177 °C
0.250 hour

@Temperature 350 °F
Recommended Cure Cycle
120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 6.00 Month

@Temperature 21.1 °C
6.00 Month

@Temperature 70.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Red
Total Product Weight (oz/yd2) 31
Arlon SQA-TMS-025