Arlon 48571R006 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 48571R006 0.0055" (0.140 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction:Side 1: Uncured RubberSide 2: Uncured RubberThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | >= 25.4 microns | >= 1.00 mil | Side 1 |
| 38.1 microns | 1.50 mil | Polyethylene Interleave | |
| >= 50.8 microns | >= 2.00 mil | Side 2 | |
| 63.5 microns | 2.50 mil | Primed Coated 1080 Fiberglass (same as 108/no plied yarns), Substrate | |
| 127 - 165 microns | 5.00 - 6.50 mil | Overall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Compound Property |
| Tensile Strength | >= 5.52 MPa | >= 800 psi | Compound Property |
| Elongation at Break | >= 550 % | >= 550 % | Compound Property |
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | [ppi], Bond Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 220 °C | 428 °F | per UL Card E54153 |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | per UL Card E54153 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Temperature 177 °C |
0.250 hour @Temperature 350 °F |
Recommended Cure Cycle |
| 120 min @Temperature 232 °C |
2.00 hour @Temperature 450 °F |
Recommended Postcure Cycle | |
| Shelf Life | 6.00 Month @Temperature <=23.9 °C |
6.00 Month @Temperature <=75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 4.5 - 5.5 | |
| Uncoated Fabric Break Strength | 40 lb/in | Fill Direction, Substrate Property |
| 70 lb/in | Warp Direction, Substrate Property |