Arlon 44602M020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate

Category Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer Arlon
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 44602M020 0.020" (0.508 mm) Cured Silicone Rubber with Fiberglass Substrate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Design/Construction:Side 1: Cured Silicone RubberAppearance Tan rubber on glass fiber fabricThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
Physical Properties Metric English Comments
Thickness 76.2 microns
3.00 mil
Polyethylene Interleave
127 microns
5.00 mil
Prime Coated 1165 Fiberglass, Substrate
381 microns
15.0 mil
Side 1
457 - 559 microns
18.0 - 22.0 mil
Overall
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Compound Property
Tensile Strength >= 6.21 MPa
>= 900 psi
Compound Property
Elongation at Break >= 300 %
>= 300 %
Compound Property
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 °C
428 °F
per UL card E54153
Minimum Service Temperature, Air -56.7 °C
-70.0 °F
Flammability, UL94 HB
HB
Compound Rated
Electrical Properties Metric English Comments
Dielectric Strength >= 15.7 kV/mm
>= 400 kV/in
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 204 °C
2.00 hour

@Temperature 400 °F
Recommended Postcure Cycle
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
From date of manufacture
Descriptive Properties Value Comments
Color Tan
Total Product Weight (oz/yd2) 19.4 - 23.4
Uncoated Fabric Break Strength 125 lb/in
Warp Direction, Substrate Property
160 lb/in
Fill Direction, Substrate Property