Arlon 44570XB025 0.025" Uncured Silicone Rubber with Fiberglass

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 44570XB025 0.025" Uncured Silicone Rubber with Fiberglass.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Interleave: 2.5 mil PolyethyleneSide 1: Uncured Silicone RubberSubstrate: Style 1165 FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	127 microns	5.00 mil	Substrate; Arlon SQA-TMS-003
	508 microns	20.0 mil	Silicone; Arlon SQA-TMS-003
	635 microns	25.0 mil	Overall Thickness; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	45	45	Silicone Property; ASTM D2240
Tensile Strength	6.38 MPa	925 psi	Silicone Property; ASTM D412
Elongation at Break	550 %	550 %	Silicone Property; ASTM D412
Peel Strength	3.86 kN/m	22.0 pli	Bond Strength; Arlon SQA-TMS-011

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	29.5 kV/mm	750 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Post Cure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 149 °C	0.250 hour @Pressure 50.0 psi, Temperature 300 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F

Descriptive Properties	Value	Comments
Color	Gray	Silicone
	White	Substrate
Total Product Weight (oz/yd2)	23.8	Arlon SQA-TMS-025