Arlon 18646B026 0.026" (0.66 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 18646B026 0.026" (0.66 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Cured Silicone RubberSubstrate: 11523 Style FiberglassSide 2: Uncured Silicone RubberInterleave: PolyethyleneThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	Side 2; Arlon SQA-TMS-024
	1.38 g/cc	0.0499 lb/in³	Side 1; Arlon SQA-TMS-024
Thickness	63.5 microns	2.50 mil	Interleave
	102 microns	4.00 mil	Side 1; Arlon SQA-TMS-003
	178 microns	7.00 mil	Side 2; Arlon SQA-TMS-003
	381 microns	15.0 mil	Substrate; Arlon SQA-TMS-003
	660 microns	26.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	51	51	Side 1; ASTM D2240
	56	56	Side 2; ASTM D2240
Tensile Strength	5.17 MPa	750 psi	Side 2; ASTM D412
	5.31 MPa	770 psi	Side 1; ASTM D412
Elongation at Break	265 %	265 %	Side 2; ASTM D412
	330 %	330 %	Side 1; ASTM D412
Tear Strength	10.5 kN/m	60.0 pli	Side 2; ASTM D624
	10.9 kN/m	62.0 pli	Side 1; ASTM D624
Peel Strength	1.45 kN/m	8.30 pli	Bond Strength; Arlon SQA-TMS-011

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	16.1 kV/mm	410 kV/in	Arlon SQA-TMS-020

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 121 °C	0.250 hour @Pressure 50.0 psi, Temperature 250 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 °C	6.00 Month @Temperature 70.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Black
Total Product Weight (oz/yd2)	29.3	Arlon SQA-TMS-025