Arlon 0.015" (0.381 mm) Layer-on-Layer Silicone Traction Motor Insulation (51229R015)

Category Polymer , Thermoset , Silicone
Manufacturer Arlon
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arlon 0.015" (0.381 mm) Layer-on-Layer Silicone Traction Motor Insulation (51229R015).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
0.005 in. (0.1 mm) minimum uncured silicone on 0.002 in. (0.5 mm) minimum cured silicone on 0.008 in. (0.2 mm) nominal Prime Coated 7628 Fiberglass; 0.003 in. (0.08 mm) polyethylene interleave; overall thickness 0.015 in ± 0.0015 (0.38 mm ± 0.038). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 566.2 g/m² ± 50.9 (16.7 oz./yd.² ± 1.5). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours. Flame Test Method: FTMS 191A, Method 5904. Maximum Flame and Glow Time: 15 seconds. Maximum Char Length: 7.62 cm (3 in).Information provided by the manufacturer, Arlon Silicone Technologies Division.
Mechanical Properties Metric English Comments
Hardness, Shore A 55 - 65
55 - 65
Tensile Strength, Ultimate >= 6.90 MPa
>= 1000 psi
Elongation at Break >= 200 %
>= 200 %
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -56.6 °C
-69.9 °F
Electrical Properties Metric English Comments
Dielectric Strength >= 15.75 kV/mm
>= 400.0 kV/in
Processing Properties Metric English Comments
Processing Temperature 176.6 °C
349.9 °F