Arlon 0.008" (0.2032 mm) Flexible Heater Silicone with Fiberglass Substrate (44571R008)

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Silicone
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 0.008" (0.2032 mm) Flexible Heater Silicone with Fiberglass Substrate (44571R008).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

0.0015 in. (0.038 mm) minimum Cured silicone rubber/Prime Coated 7628 Fiberglass/ 0.0015 in (0.038 mm) minimum uncured silicone rubber; 0.0015 in. (0.038 mm) polyethylene interleave; overall thickness 0.008 in. + 0.001,-0.0005 (0.2 mm +0.02, -0.01). The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 281.4 g/m² ± 30.52 (8.3 oz./yd.² ± 0.9). Shelf Life: 6 months from date of manufacture at 23.8°C (75°F). Cure Time: 0.25 hours. Post Cure: 204°C (400°F), for 2 hours.Information provided by the manufacturer, Arlon Silicone Technologies Division.

Mechanical Properties	Metric	English
Hardness, Shore A	40 - 50	40 - 50
Tensile Strength, Ultimate	5.58 - 6.82 MPa	809 - 989 psi
Elongation at Yield	540 - 660 %	540 - 660 %

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	200 °C	392 °F	Mechanical per UL Card E54153
	232 °C	450 °F
Minimum Service Temperature, Air	-56.6 °C	-69.9 °F
UL RTI, Electrical	220 °C	428 °F	per UL Card E54153
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.75 kV/mm	>= 400.0 kV/in

Processing Properties	Metric	English	Comments
Processing Temperature	176.6 °C	349.9 °F	curing temp., at 0.345 MPa (50 psi)