Arkema Group Rilsan® PA 11 G BMNO MED Nylon 11

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Unreinforced
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® PA 11 G BMNO MED Nylon 11.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rilsan® PA 11 G BMNO MED is a polyamide produced from a renewable source. This grade offers the highest quality and it is specially designed to meet the stringent requirements of the medical applications such as minimally invasive devices. RILSAN® PA 11 G BMNO MED also offers an excellent combination of properties. Upon request letters regarding USP Class VI testing can be provided. Designation: PA11, MHLR, 12-010Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Water Absorption 0.95 %

@Temperature 23.0 °C,
Time 86400 sec
0.95 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.75 %

@Temperature 20.0 °C
0.75 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 2.00 mm,
Time 86400 sec
0.0040 in/in

@Thickness 0.0787 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Thickness 2.00 mm,
Time 86400 sec
0.0080 in/in

@Thickness 0.0787 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 68
68
After 15 sec, Conditioned 15 days at 23°C - 50% RH; ISO 868
75
75
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 58.0 MPa
8410 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Strength, Yield 41.0 MPa
5950 psi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Break <= 200 %
<= 200 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Elongation at Yield 5.0 %
5.0 %
Conditioned 15 days at 23°C - 50% RH; ISO 527
Tensile Modulus 1.28 GPa
186 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 527
Flexural Modulus 1.14 GPa
165 ksi
Conditioned 15 days at 23°C - 50% RH; ISO 178
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 189 °C
372 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
Processing Properties Metric English Comments
Nozzle Temperature 240 - 290 °C
464 - 554 °F
270 °C
518 °F
Recommended
Mold Temperature 25.0 - 60.0 °C
77.0 - 140 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Bio Based Carbon 100%
ASTM 6866, Calculation