Arkema Group Rilsan® Clear G170 Polyamide

Category Polymer , Thermoplastic , Nylon
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® Clear G170 Polyamide.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rilsan® Clear G170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications and for medical uses.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO R 1183 D
Water Absorption 1.3 %
1.3 %
at equilibrium at 23°C and 50 % RH; ISO 62
3.2 %
3.2 %
at equilibrium at 23°C in water; ISO 62
Mechanical Properties Metric English Comments
Hardness, Shore D 84
84
instantaneous, conditioned 15 day, 23°C - 50 % R.H.; ISO 868
79

@Time 15.0 sec
79

@Time 0.00417 hour
conditioned 15 day, 23°C - 50 % R.H.; ISO 868
Tensile Strength at Break 58.0 MPa
8410 psi
conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Tensile Strength, Yield 74.0 MPa
10700 psi
conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Elongation at Break >= 100 %
>= 100 %
conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Elongation at Yield 9.0 %
9.0 %
conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Tensile Modulus 2.02 GPa
293 ksi
conditioned 15 days, 23°C - 50 % R.H.; ISO 527
Flexural Modulus 1.98 GPa
287 ksi
conditioned 15 days, 23°C - 50 % R.H.; ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 130 J/cm²

@Temperature 23.0 °C
619 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
130 J/cm²

@Temperature -30.0 °C
619 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
ISO 75
Glass Transition Temp, Tg 168 °C
334 °F
ISO 11357
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
clear; thickness not quantified
Processing Properties Metric English Comments
Processing Temperature 270 - 290 °C
518 - 554 °F
Extrusion
280 °C
536 °F
Extrusion, recommended
270 - 310 °C
518 - 590 °F
Injection
290 °C
554 °F
Injection, recommended
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Transparency 90.8%
560 nm, 2 mm; ISO 13168-1,2