- Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Conditioned)
Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 20% Glass Fiber Filler |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA11,MS,18-040,(G+C)(F+D)(25+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Additive free.Rigidity. Low friction coefficient. Abrasion resistance. High compressive strength. Low linear expansion coefficient. Low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability.UL classification: UL94 HB RTI(C) 65/65/65Example applications: Mechanical parts with friction such as gear or bearing.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 108 MPa | 15700 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 7.30 GPa | 1060 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.40 J/cm² | 35.2 ft-lb/in² | |
| 8.29 J/cm² @Temperature -30.0 °C |
39.5 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.25 J/cm² | 5.95 ft-lb/in² | |
| 0.990 J/cm² @Temperature -30.0 °C |
4.71 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | |
| Surface Resistance | 6.00e+12 ohm | 6.00e+12 ohm | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | |
| Comparative Tracking Index | 300 V | 300 V |