Arkema Group Rilsan® BUM 30 Nylon 11, 30% Glass Bead Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® BUM 30 Nylon 11, 30% Glass Bead Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA11,M,18-020,GB30Rigid grade with glass beads (30%) filler for injection molding. Available colors: black and natural. Additive free.Outstanding isotropic properties. High compressive strength. Low and homogeneous shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption).Water potable contact approval WRC 950 1509. UL classification: UL94 HB RTI(C) 65/65/65Example applications: Mechanical parts with high dimensional precision.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 235 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 39.0 MPa
5660 psi
50 mm/min
Elongation at Break 40 %
40 %
Nominal Strain; 50 mm/min
Elongation at Yield 4.0 %
4.0 %
50 mm/min
Tensile Modulus 1.94 GPa
281 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
7.33 J/cm²

@Temperature -30.0 °C
34.9 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.510 J/cm²
2.43 ft-lb/in²
0.460 J/cm²

@Temperature -30.0 °C
2.19 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 20.0 °C
38.9 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 165 °C
329 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 40.0 kV/mm
1020 kV/in
Comparative Tracking Index 600 V
600 V