Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® BMN Y BZ TL Nylon 11, Bronze Bead Filled (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA11,MHLS,16-020,(Z+M)(B+D)(80BZ+05)Rigid grade with bronze beads (85%) and molybdenum fillers for injection molding. Available color: steel brown. Light and heat stabilized.No need of lubricant. Low friction coefficient. High density (d=4). Outstanding compressive strength. High thermal conductivity. High dimensional stability (low moisture absorption).Example applications: Auto-lubricating bearing.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.80 g/cc | 0.137 lb/in³ | |
| Melt Flow | 17.7 g/10 min @Load 5.00 kg, Temperature 235 °C |
17.7 g/10 min @Load 11.0 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 4.60 GPa | 667 ksi | 1 mm/min |
| Charpy Impact Unnotched | 1.69 J/cm² | 8.04 ft-lb/in² | |
| 1.96 J/cm² @Temperature -30.0 °C |
9.33 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.390 J/cm² | 1.86 ft-lb/in² | |
| 0.380 J/cm² @Temperature -30.0 °C |
1.81 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 183 °C | 361 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10000 ohm-cm | 10000 ohm-cm |