Arkema Group Rilsan® BECN TL Nylon 11, Sheathing Grade (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11, Cable Sheathing Grade
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® BECN TL Nylon 11, Sheathing Grade (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA11,KHL,12-010Rigid grade for sheathing of wires and cables. Available color: natural. Light and heat stabilized.High abrasion resistance. Well adapted melt viscosity. Ability to be processed in thin wall thickness.UL classification: UL94 V2; RTI(C) 65/65/65Example applications: Coating of electrical and telephone cables, loose tubes for optical fiber.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
Melt Flow 29.8 g/10 min

@Load 2.16 kg,
Temperature 235 °C
29.8 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 MPa
5800 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 10 %
10 %
50 mm/min
Tensile Modulus 1.44 GPa
209 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB
NB
Low Temp
Charpy Impact, Notched 1.40 J/cm²
6.66 ft-lb/in²
1.06 J/cm²

@Temperature -30.0 °C
5.04 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 20.0 °C
50.0 µin/in-°F

@Temperature 68.0 °F
Melting Point 183 °C
361 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 160 °C
320 °F
50°C/hr; 50N
UL RTI, Electrical 65.0 °C
149 °F
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL RTI, Mechanical without Impact 65.0 °C
149 °F
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.20 mm
V-2

@Thickness 0.126 in
Oxygen Index 25 %
25 %
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Strength 30.0 kV/mm
762 kV/in
Comparative Tracking Index 600 V
600 V