Arkema Group Rilsan® AZM 43 G9 T6LD Nylon 12, 43% Glass Fiber Filled (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 40% Glass Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AZM 43 G9 T6LD Nylon 12, 43% Glass Fiber Filled (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,MHLS,16-080,(G+C)(F+D)(43+05)Rigid grade with glass fiber (43%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stabilizing agent. Mold-release agent.High rigidity. Low friction coefficient. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Mechanical parts with friction such as gear and bearing.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
Water Absorption 1.0 %
1.0 %
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 235 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 138 MPa
20000 psi
5 mm/min
Elongation at Break 4.0 %
4.0 %
5 mm/min
Tensile Modulus 13.3 GPa
1930 ksi
1 mm/min
Charpy Impact Unnotched 6.87 J/cm²
32.7 ft-lb/in²
6.87 J/cm²

@Temperature -30.0 °C
32.7 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.26 J/cm²
6.00 ft-lb/in²
1.06 J/cm²

@Temperature -30.0 °C
5.04 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in