Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 30% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AZM 30 GT8LD Nylon 12, 30% Glass Fiber Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12,MHLS,16-050,(G+C)(F+D)(30+05)Rigid grade with glass fiber (30%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stabilizing agent. Mold-release agent.High rigidity. Low friction coefficient. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Mechanical parts with friction such as knuckle joint for windshield wiper.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 114 MPa | 16500 psi | 5 mm/min |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min |
| Tensile Modulus | 8.75 GPa | 1270 ksi | 1 mm/min |
| Charpy Impact Unnotched | 9.30 J/cm² | 44.3 ft-lb/in² | |
| 9.11 J/cm² @Temperature -30.0 °C |
43.4 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.77 J/cm² | 8.42 ft-lb/in² | |
| 1.35 J/cm² @Temperature -30.0 °C |
6.42 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dissipation Factor | 0.00036 @Frequency 1e+6 Hz |
0.00036 @Frequency 1e+6 Hz |
|
| 0.00045 @Frequency 100 Hz |
0.00045 @Frequency 100 Hz |