Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, 20% Glass Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AZM 23 G9 T6LD Nylon 12, 23% Glass Fiber Filled (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,MHLR,16-050,(G+C)(F+D)(23+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Reinforced light and heat stabilizing agent. Mold-release agent.Rigidity. Low friction coefficient. High compressive strength. Very low shrinkage: include 0,5% on average for the design of the mold. Low coefficient of linear expansion. High dimensional stability.Example applications: Mechanical parts with friction such as gear and bearing.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Water Absorption 1.1 %
1.1 %
Melt Flow 3.7 g/10 min

@Load 2.16 kg,
Temperature 235 °C
3.7 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 104 MPa
15100 psi
5 mm/min
Elongation at Break 5.0 %
5.0 %
5 mm/min
Tensile Modulus 7.11 GPa
1030 ksi
1 mm/min
Charpy Impact Unnotched 7.13 J/cm²
33.9 ft-lb/in²
7.91 J/cm²

@Temperature -30.0 °C
37.6 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.29 J/cm²
6.14 ft-lb/in²
0.950 J/cm²

@Temperature -30.0 °C
4.52 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Dielectric Strength 17.5 kV/mm
445 kV/in
Dissipation Factor 0.000335

@Frequency 1e+6 Hz
0.000335

@Frequency 1e+6 Hz
0.000369

@Frequency 100 Hz
0.000369

@Frequency 100 Hz
Comparative Tracking Index 100 V
100 V