Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Carbon Fiber Filled
Manufacturer Arkema
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® ASR 20 Nylon 12, 20% Carbon Fiber Filled (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12,M,16-090,CF20Rigid grade with carbon fiber filler (20%) for injection molding. Available color: black. High strength-to-weight ratio. Very low shrinkage: include 0,5% on average for the design of the mold. High dimensional stability (low moisture absorption). Antistatic properties.Example applications: Parts with high mechanical properties and dimensional precision.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
Melt Flow 4.6 g/10 min

@Load 2.16 kg,
Temperature 235 °C
4.6 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 128 MPa
18600 psi
5 mm/min
Elongation at Break 4.0 %
4.0 %
5 mm/min
Tensile Modulus 11.4 GPa
1650 ksi
1 mm/min
Charpy Impact Unnotched 6.37 J/cm²
30.3 ft-lb/in²
5.83 J/cm²

@Temperature -30.0 °C
27.7 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 1.73 J/cm²
8.23 ft-lb/in²
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 40.0 µm/m-°C

@Temperature 20.0 °C
22.2 µin/in-°F

@Temperature 68.0 °F
Melting Point 174 °C
345 °F
(Dry)
Deflection Temperature at 0.46 MPa (66 psi) 175 °C
347 °F
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Vicat Softening Point 170 °C
338 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Electrical Resistivity 600 ohm-cm
600 ohm-cm
Dielectric Strength 1.00 kV/mm
25.4 kV/in
Comparative Tracking Index 100 V
100 V