Arkema Group Rilsan® AMN P30 LD Nylon 12, Flexible, Injection Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AMN P30 LD Nylon 12, Flexible, Injection Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12-P,MLR,12-004Flexible grade for injection molding. Available color: black. Light stabilized. Mold-release agent.Good impact strength. Flexibility and dynamic properties. Easy filling of the mold due to its well adapted viscosity. Low shrinkage: include 1% on average for the design of the mold. Good dimensional stability (low moisture absorption).UL classification: UL94 HB RTI(C) 65/65/65.Example applications: Cable ties and clips.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Melt Flow | 61.3 g/10 min @Load 2.16 kg, Temperature 235 °C |
61.3 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 22 % | 22 % | 50 mm/min |
| Tensile Modulus | 0.545 GPa | 79.0 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 2.17 J/cm² | 10.3 ft-lb/in² | |
| 0.370 J/cm² @Temperature -30.0 °C |
1.76 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 168 °C | 334 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | |
| Vicat Softening Point | 133 °C | 271 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Surface Resistance | 5.00e+11 ohm | 5.00e+11 ohm | |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| Comparative Tracking Index | 600 V | 600 V |