Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | Arkema |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Designation ISO 1874-PA12-P,MHLR,14-005Flexible grade for injection molding. Available colors: black and natural. Light and heat stabilized. Mold-release agent.Good impact strength. Flexibility and dynamic properties. Easy filling of the mold due to its well adapted viscosity. Low shrinkage: include 1% on average for the design of the mold. Good dimensional stability (low moisture absorption).Example applications: Flexible parts with high impact strength and vibration resistance.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Melt Flow | 42 g/10 min @Load 2.16 kg, Temperature 235 °C |
42 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 19 % | 19 % | 50 mm/min |
| Tensile Modulus | 0.570 GPa | 82.7 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.77 J/cm² | 8.42 ft-lb/in² | |
| 0.410 J/cm² @Temperature -30.0 °C |
1.95 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 20.0 °C |
66.7 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | |
| Vicat Softening Point | 134 °C | 273 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.10 mm |
HB @Thickness 0.122 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | |
| Comparative Tracking Index | 600 V | 600 V |