Arkema Group Plexiglas® V045 Acrylic

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, General Purpose, Molded
Manufacturer Arkema
Trade Name Plexiglas®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Plexiglas® V045 Acrylic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plexiglas® V045 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its chemical and heat resistance as well a high melt flow. Plexiglas® V045 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V045 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.Appearance: Clear/Transparent; Colors Available; TranslucentCharacteristics: High Clarity; High Scratch Resistance; Good Color Stability, Good Dimensional Stability; Low Shrinkage; Good Thermal Stability, Good UV Stability; Medium Heat Resistance; Good Weather ResistanceApplications: Lighting Diffusers
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Water Absorption 0.30 %
0.30 %
weight gain after 24 hr. immersion; ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Melt Flow 2.3 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.3 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 91
91
ASTM D785
Tensile Strength, Ultimate 70.3 MPa
10200 psi
ASTM D638
Elongation at Break 6.00 %
6.00 %
ASTM D638
Tensile Modulus 3.10 GPa
450 ksi
ASTM D638
Flexural Strength <= 103 MPa
<= 15000 psi
ASTM D790
Flexural Modulus 3.10 GPa
450 ksi
ASTM D790
Izod Impact, Notched 0.160 J/cm
0.300 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.187 W/m-K
1.30 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 94.4 °C
202 °F
annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 92.8 °C
199 °F
annealed; ASTM D648
Vicat Softening Point 97.2 °C
207 °F
50°C/hr; 50N; ASTM D1525
103 °C
217 °F
50°C/hr; 10N; ASTM D1525
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Refractive Index 1.49

@Temperature 22.8 °C
1.49

@Temperature 73.0 °F
N<sub>D</sub>; ASTM D542
Haze <= 1.0 %

@Thickness 3.17 mm
<= 1.0 %

@Thickness 0.125 in
ASTM D1003
Transmission, Visible 92 %

@Thickness 3.17 mm
92 %

@Thickness 0.125 in
ASTM D1003