Arkema Group Plexiglas® SG10 Acrylic

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Gamma Radiation Resistant, Molded
Manufacturer Arkema
Trade Name Plexiglas®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Plexiglas® SG10 Acrylic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plexiglas® SG10 is an impact-modified acrylic resin suitable for injection molding and extrusion. It is a high flow resin designed to provide outstanding light transmission and water white clarity for disposable medical applications.Some of the features and benefits of Plexiglas® SG10 areChemical Resistance: Good resistance to lipids and drug formulations, Good resistance to isopropyl alcohol (IPA), Property retention after exposure to hospital antiseptics, acids and basesSterilization: Stable to gamma radiation, E-beam, and ETO, Rapid recovery with excellent color stability, Retention of transparency and clarity, Retention of mechanical propertiesDurability and Processability: Moldflow simulation data available, Excellent melt processability, Reduced cycle times, Suitable for thin-wall applications and complex multi-cavity molds, Good bondability using solvent, ultrasonic, or radio frequency methodsAppearance:Clear/TransparentCharacteristics:Alcohol Resistant; Biocompatible; Bondability; BPA Free; Chemical Resistant; High Clarity; ESCR, High (Stress Crack Resist.); High Impact Resistance; Good Moldability; Radiation (Gamma) Resistant; Sterilization, E-beam; Sterilization, Ethylene OxideApplications:Medical/Healthcare Applications; Medical AppliancesAgency Ratings:ISO 10993-4; ISO 10993-5; USP CLASS VI
Physical Properties Metric English Comments
Specific Gravity 1.15 g/cc
1.15 g/cc
ASTM D792
Water Absorption 0.40 %
0.40 %
weight gain after 24 hr. immersion; ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0080 cm/cm
0.0030 - 0.0080 in/in
ASTM D955
Melt Flow 3.3 g/10 min

@Load 3.80 kg,
Temperature 230 °C
3.3 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 38
38
ASTM D785
Tensile Strength, Ultimate 36.5 MPa
5300 psi
ASTM D638
Elongation at Break 50.0 %
50.0 %
ASTM D638
Tensile Modulus 1.86 GPa
270 ksi
ASTM D638
Flexural Strength <= 71.0 MPa
<= 10300 psi
ASTM D790
Flexural Modulus 1.86 GPa
270 ksi
ASTM D790
Izod Impact, Notched 0.481 J/cm
0.900 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Thermal Conductivity 0.216 W/m-K
1.50 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C
190 °F
annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.8 °C
181 °F
annealed; ASTM D648
Vicat Softening Point 80.0 °C
176 °F
50°C/hr; 50N; ASTM D1525
92.8 °C
199 °F
50°C/hr; 10N; ASTM D1525
Flammability, UL94 HB
HB
Optical Properties Metric English Comments
Refractive Index 1.49

@Temperature 22.8 °C
1.49

@Temperature 73.0 °F
N<sub>D</sub>; ASTM D542
Haze <= 2.0 %

@Thickness 3.17 mm
<= 2.0 %

@Thickness 0.125 in
ASTM D1003
Transmission, Visible 91 %

@Thickness 3.17 mm
91 %

@Thickness 0.125 in
ASTM D1003