Arkema Group Pebax® MX 1205 SA 01 Polyether Block Amide (PEBA)

Category Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer Arkema
Trade Name Pebax®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Pebax® MX 1205 SA 01 Polyether Block Amide (PEBA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether block amide PEBAX® MX 1205 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Water Absorption 1.2 %

@Temperature 23.0 °C,
Time 86400 sec
1.2 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.40 %

@Temperature 20.0 °C
0.40 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.0040 in/in

@Thickness 0.157 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.011 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.011 in/in

@Thickness 0.157 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 46
46
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
41

@Time 15.0 sec
41

@Time 0.00417 hour
Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 42.0 MPa
6090 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break >= 550 %
>= 550 %
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus 0.0860 GPa
12.5 ksi
Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 147 °C
297 °F
ISO 11357
Vicat Softening Point 111 °C

@Load 1.02 kg
232 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 °C
428 °F
Recommended Extrusion Temperature
210 - 230 °C
410 - 446 °F
Extrusion Range
Nozzle Temperature 200 - 270 °C
392 - 518 °F
240 °C
464 °F
Recommended
Mold Temperature 10.0 - 30.0 °C
50.0 - 86.0 °F
Drying Temperature 60.0 - 70.0 °C
140 - 158 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour