Arkema Group Pebax® 5533 SA 01 Polyether Block Amide (PEBA)

Category Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer Arkema
Trade Name Pebax®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Pebax® 5533 SA 01 Polyether Block Amide (PEBA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyether block amide PEBAX® 5533 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Water Absorption 1.2 %

@Temperature 23.0 °C,
Time 86400 sec
1.2 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 0.60 %

@Temperature 20.0 °C
0.60 %

@Temperature 68.0 °F
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.012 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.012 in/in

@Thickness 0.157 in,
Time 24.0 hour
Linear Mold Shrinkage, Transverse 0.014 cm/cm

@Thickness 4.00 mm,
Time 86400 sec
0.014 in/in

@Thickness 0.157 in,
Time 24.0 hour
Mechanical Properties Metric English Comments
Hardness, Shore D 54
54
Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
50

@Time 15.0 sec
50

@Time 0.00417 hour
Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break 52.0 MPa
7540 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break >= 450 %
>= 450 %
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus 0.170 GPa
24.7 ksi
Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Melting Point 159 °C
318 °F
ISO 11357
Vicat Softening Point 142 °C

@Load 1.02 kg
288 °F

@Load 2.25 lb
ISO 306
Processing Properties Metric English Comments
Processing Temperature 220 °C
428 °F
Recommended Extrusion Temperature
210 - 230 °C
410 - 446 °F
Extrusion Range
Nozzle Temperature 200 - 270 °C
392 - 518 °F
240 °C
464 °F
Recommended
Mold Temperature 25.0 - 60.0 °C
77.0 - 140 °F
Drying Temperature 65.0 - 75.0 °C
149 - 167 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour