Arkema Group Pebax® 4033 SA 01 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 4033 SA 01 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyether block amide PEBAX® 4033 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % @Temperature 23.0 °C, Time 86400 sec |
1.2 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 0.50 % @Temperature 20.0 °C |
0.50 % @Temperature 68.0 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 4.00 mm, Time 86400 sec |
0.0040 in/in @Thickness 0.157 in, Time 24.0 hour |
|
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 4.00 mm, Time 86400 sec |
0.011 in/in @Thickness 0.157 in, Time 24.0 hour |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 42 | 42 | Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868 |
| 35 @Time 15.0 sec |
35 @Time 0.00417 hour |
Conditioned 15 days at 23°C - 50% RH; ISO 868 | |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Elongation at Break | >= 450 % | >= 450 % | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Flexural Modulus | 0.0770 GPa | 11.2 ksi | Conditioned 15 days at 23°C - 50% RH; ISO178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | ISO 11357 |
| Vicat Softening Point | 131 °C @Load 1.02 kg |
268 °F @Load 2.25 lb |
ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 °C | 428 °F | Recommended Extrusion Temperature |
| 210 - 230 °C | 410 - 446 °F | Extrusion Range | |
| Nozzle Temperature | 200 - 270 °C | 392 - 518 °F | |
| 240 °C | 464 °F | Recommended | |
| Mold Temperature | 10.0 - 30.0 °C | 50.0 - 86.0 °F | |
| Drying Temperature | 60.0 - 70.0 °C | 140 - 158 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |