Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **)

Category	Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Extruded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Oroglas® V 044 Acrylic, Extrusion Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OROGLAS V 044 is an extrusion grade offering good compromise between physical properties and thermal resistance.OROGLAS V 044 is recommended for extrusion of profiles, tubes and sheets.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³
Water Absorption	1.9 %	1.9 %
Moisture Absorption at Equilibrium	0.30 %	0.30 %	Humidity Absorption
Melt Flow	1.5 g/10 min @Load 3.80 kg, Temperature 230 °C	1.5 g/10 min @Load 8.38 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	86.0 MPa	12500 psi	50 mm/min
Elongation at Break	6.0 %	6.0 %	Nominal Strain; 50 mm/min
Tensile Modulus	3.30 GPa	479 ksi	1 mm/min
Charpy Impact Unnotched	2.00 J/cm²	9.52 ft-lb/in²
Charpy Impact, Notched	0.200 J/cm²	0.952 ft-lb/in²
Tensile Creep Modulus, 1 hour	2700 MPa	392000 psi
Tensile Creep Modulus, 1000 hours	1800 MPa	261000 psi

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	65.0 µm/m-°C @Temperature 20.0 °C	36.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	96.0 °C	205 °F
Deflection Temperature at 1.8 MPa (264 psi)	93.0 °C	199 °F
Vicat Softening Point	96.0 °C	205 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Optical Properties	Metric	English	Comments
Transmission, Visible	80 %	80 %	Mfr. reports 'Transparent' but doesn't quantify.

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	3.2 @Frequency 1e+6 Hz	3.2 @Frequency 1e+6 Hz
	3.7 @Frequency 100 Hz	3.7 @Frequency 100 Hz
Dielectric Strength	19.7 kV/mm	500 kV/in
Dissipation Factor	0.040 @Frequency 1e+6 Hz	0.040 @Frequency 1e+6 Hz
	0.050 @Frequency 100 Hz	0.050 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V