Arkema Group Oroglas® DRT Acrylic, Impact Grade  (discontinued **)

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Oroglas® DRT Acrylic, Impact Grade  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
For extrusion and injection molding applications. OROGLAS DRT combines good thermal resistance with an excellent impact resistance.Key features : impact resistance: up to 10 times more impact-resistant than standard acrylic high temperature resistance: HDT A / 1.82 MPa = 88°c clarity and low haze UV stability easy processing Typical applications: indoor and outdoor lighting applications appliances and house ware items automotive signs OROGLAS DRT is also used as top layer, alone or in coextrusion for sanitary, garden furniture, pools, window profiles and automotive fields.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Water Absorption 2.0 %
2.0 %
Moisture Absorption at Equilibrium 0.36 %
0.36 %
Humidity Absorption
Melt Flow 0.80 g/10 min

@Load 3.80 kg,
Temperature 230 °C
0.80 g/10 min

@Load 8.38 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min
Elongation at Break 40 %
40 %
Nominal Strain; 50 mm/min
Elongation at Yield 5.0 %
5.0 %
50 mm/min
Tensile Modulus 1.70 GPa
247 ksi
1 mm/min
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Tensile Creep Modulus, 1 hour 1400 MPa
203000 psi
Tensile Creep Modulus, 1000 hours 1000 MPa
145000 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature 20.0 °C
55.6 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C
199 °F
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Vicat Softening Point 93.0 °C
199 °F
50°C/hr; 50N
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
Mfr. reports 'Transparent' but doesn't quantify.
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 3.2

@Frequency 1e+6 Hz
3.2

@Frequency 1e+6 Hz
3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
Dielectric Strength 15.0 kV/mm
381 kV/in
Dissipation Factor 0.040

@Frequency 1e+6 Hz
0.040

@Frequency 1e+6 Hz
0.050

@Frequency 100 Hz
0.050

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V