Arkema Group Orgalloy® RS 76E101 Nylon 66 Alloy, Rigid Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 76E101 Nylon 66 Alloy, Rigid Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RS 66 series, rigid polyamide 66 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.Impact modified, high fluidity. For injection molding of large parts.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Water Absorption | 2.8 % | 2.8 % | |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | Humidity Absorption |
| Melt Flow | 18 g/10 min @Load 5.00 kg, Temperature 275 °C |
18 g/10 min @Load 11.0 lb, Temperature 527 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 4.2 % | 4.2 % | 50 mm/min |
| Tensile Modulus | 1.60 GPa | 232 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature 20.0 °C |
72.2 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 142 µm/m-°C @Temperature 20.0 °C |
78.9 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 255 °C | 491 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 148 °C | 298 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 1.9 @Frequency 100 Hz |
1.9 @Frequency 100 Hz |
|
| 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |