Arkema Group Orgalloy® RS 60E10TL Nylon 6 Alloy, Rigid Grade (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Arkema
Trade Name Orgalloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Orgalloy® RS 60E10TL Nylon 6 Alloy, Rigid Grade (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties. Impact modified - Balanced properties between stiffness and impact resistance at low temperatures. Better UV resistance.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
Water Absorption 3.2 %
3.2 %
Moisture Absorption at Equilibrium 1.3 %
1.3 %
Humidity Absorption
Melt Flow 14 g/10 min

@Load 5.00 kg,
Temperature 235 °C
14 g/10 min

@Load 11.0 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 42.0 MPa
6090 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 4.5 %
4.5 %
50 mm/min
Tensile Modulus 1.62 GPa
235 ksi
1 mm/min
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature 20.0 °C
61.1 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 143 µm/m-°C

@Temperature 20.0 °C
79.4 µin/in-°F

@Temperature 68.0 °F
Melting Point 220 °C
428 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
Dielectric Constant 2.5

@Frequency 100 Hz
2.5

@Frequency 100 Hz
3.1

@Frequency 1e+6 Hz
3.1

@Frequency 1e+6 Hz
Dielectric Strength 38.0 kV/mm
965 kV/in
Dissipation Factor 0.025

@Frequency 1e+6 Hz
0.025

@Frequency 1e+6 Hz
0.070

@Frequency 100 Hz
0.070

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V