Arkema Group Orgalloy® RS 6010 Nylon 6 Alloy, 10% Glass Fiber Reinforced (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer	Arkema
Trade Name	Orgalloy®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Orgalloy® RS 6010 Nylon 6 Alloy, 10% Glass Fiber Reinforced (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.RS 6010: 10 % glass fiber, balanced properties between impact resistance, stiffness, density. For injection molding and for extrusion of profiles.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³
Water Absorption	3.0 %	3.0 %
Moisture Absorption at Equilibrium	1.2 %	1.2 %	Humidity Absorption
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 235 °C	6.0 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	80.0 MPa	11600 psi	5 mm/min
Elongation at Break	4.8 %	4.8 %	5 mm/min
Tensile Modulus	3.30 GPa	479 ksi	1 mm/min
Tensile Creep Modulus, 1 hour	2530 MPa	367000 psi
Tensile Creep Modulus, 1000 hours	1790 MPa	260000 psi

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm
Dielectric Constant	2.6 @Frequency 100 Hz	2.6 @Frequency 100 Hz
	3.2 @Frequency 1e+6 Hz	3.2 @Frequency 1e+6 Hz
Dielectric Strength	36.0 kV/mm	914 kV/in
Dissipation Factor	0.024 @Frequency 1e+6 Hz	0.024 @Frequency 1e+6 Hz
	0.063 @Frequency 100 Hz	0.063 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V