Arkema Group Orgalloy® R 60 ES Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® R 60 ES Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO R1183 |
| Water Absorption | 1.0 % | 1.0 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C / 50% RH; ISO 62 |
| 3.3 % | 3.3 % | in 23°C water; ISO 62 | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ISO 868 |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ISO R527 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO R527 |
| Elongation at Break | 220 % | 220 % | ISO R527 |
| Elongation at Yield | 3.4 % | 3.4 % | ISO R527 |
| Modulus of Elasticity | 2.01 GPa | 292 ksi | ISO R527 |
| Flexural Strength | 63.0 MPa | 9140 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 73.0 MPa | 10600 psi | Dry; ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 2.20 GPa | 319 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
Dry; ISO 179/Af | |
| 12.0 J/cm² @Temperature -20.0 °C |
57.1 ft-lb/in² @Temperature -4.00 °F |
Dry; ISO 179/Af | |
| 14.0 J/cm² @Temperature -20.0 °C |
66.6 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 2030 MPa | 294000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 93.0 µm/m-°C @Temperature 20.0 - 60.0 °C |
51.7 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 130 µm/m-°C @Temperature 20.0 - 60.0 °C |
72.2 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO R75 |
| Vicat Softening Point | 130 °C | 266 °F | 50 N - B method; ISO 306 |
| 215 °C | 419 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB | |
| Flame Spread | 17 mm/min | 0.67 in/min | FMVSS 302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+15 ohm-cm | 1.60e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 4.80e+15 ohm | 4.80e+15 ohm | ASTM D257 |
| Dielectric Strength | 38.0 kV/mm @Thickness 1.00 mm |
965 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.025 @Frequency 100000 Hz |
0.025 @Frequency 100000 Hz |
NFC 26 230 |
| 0.062 @Frequency 100 Hz |
0.062 @Frequency 100 Hz |
NFC 26 230 | |
| 0.065 @Frequency 1000 Hz |
0.065 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive classification | E-3 | FMVSS 302 |