Arkema Group Orgalloy® LT 5050 Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LT 5050 Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO R1183 |
| Water Absorption | 1.35 % | 1.35 % | 23°C / 24 hrs; ISO 62 |
| Melt Flow | 2.0 g/10 min @Load 5.00 kg, Temperature 235 °C |
2.0 g/10 min @Load 11.0 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ISO 868 |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO R527 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO R527 |
| Elongation at Break | 260 % | 260 % | ISO R527 |
| Elongation at Yield | 3.5 % | 3.5 % | ISO R527 |
| Modulus of Elasticity | 0.460 GPa | 66.7 ksi | ISO R527 |
| Flexural Modulus | 0.500 GPa | 72.5 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 0.800 GPa | 116 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
ISO 179/Af |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 420 MPa | 60900 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 - 60.0 °C |
94.4 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 180 µm/m-°C @Temperature 20.0 - 60.0 °C |
100 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Vicat Softening Point | 198 °C | 388 °F | 10 N - A method; ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.40e+13 ohm-cm | 7.40e+13 ohm-cm | ASTM D257 |
| Surface Resistance | 3.10e+15 ohm | 3.10e+15 ohm | ASTM D257 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.00 mm |
914 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.050 @Frequency 100000 Hz |
0.050 @Frequency 100000 Hz |
NFC 26 230 |
| 0.11 @Frequency 100 Hz |
0.11 @Frequency 100 Hz |
NFC 26 230 | |
| 0.11 @Frequency 1000 Hz |
0.11 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Raschig Group PiMC 1841 Metallic colors
- Michelman® Michem® Emulsion 47950 Nonionic paraffin emulsion
- Sylvin Technologies 9940-80 Natural PVC Molding Compound
- Universal Wire Works 5056 (AMS 4182) Aluminum Alloy Filler Metal
- Ensinger Tecamid® HS Nylon (PA)
- Eurotec® Tecomid® NB40 GR30 NL HW PA6, 30% glass fiber reinforced, hydrolysis stabilized, natural
- Arlon 28601M015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- ACC MM925 Condensation Cure 2-Part Molding Rubber
- BASF Ultramid® B36 01 PA6 (Dry)
- DuPont Performance Polymers Zytel® 101F NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved