Arkema Group Orgalloy® LE 60 SF Polyamide Alloy
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® LE 60 SF Polyamide Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 23°C / 50% RH; ISO 62 |
| 5.5 % | 5.5 % | in 23°C water; ISO 62 | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 68 | 68 | ISO 868 |
| Tensile Strength, Ultimate | 56.0 MPa | 8120 psi | ISO R527 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ISO R527 |
| Elongation at Break | 280 % | 280 % | ISO R527 |
| Elongation at Yield | 4.1 % | 4.1 % | ISO R527 |
| Modulus of Elasticity | 1.35 GPa | 196 ksi | ISO R527 |
| Flexural Strength | 41.0 MPa | 5950 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.850 GPa | 123 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 1.35 GPa | 196 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.90 J/cm² | 13.8 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 21.0 J/cm² @Temperature -20.0 °C |
99.9 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 1150 MPa | 167000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Vicat Softening Point | 99.0 °C | 210 °F | 50 N - B method; ISO 306 |
| 206 °C | 403 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FE-5642Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- NOVA Chemicals Novapol® LF-Y819-C LDPE Film Resin
- Kingfa JH960 6300 Non-halogenated Flame Retardant PC/ABS Alloy
- LATI Laticonther 88/10 GR/50 PEEK, 50% Graphite Reinforced
- SABIC Innovative Plastics LNP STAT-KON DE0021E PC
- Shakespeare NX-315 diameter 0.13 mm Nylon 66 Monofilament
- ChevronTexaco Clarity® ISO 460 Synthetic Paper Machine Oil
- Arlon 32210A005 0.005" (0.127 mm) Uncured Fluorosilicone Rubber on Polyester Carrier
Copyright © lookpolymers.com All Rights Reserved