Arkema Group LOTADER® TX 8030 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category	Polymer , Adhesive , Thermoplastic , EMAAA Terpolymer
Manufacturer	Arkema
Trade Name	LOTADER®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group LOTADER® TX 8030 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LOTADER TX 8030 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high pressure autoclave process. LOTADER TX 8030 is an adhesive designed for extrusion coating and extrusion lamination of paper, aluminum and polyethylene films. LOTADER TX 8030 can be used pure or blended with polyethylene.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	0.940 g/cc @Temperature 23.0 °C	0.0340 lb/in³ @Temperature 73.4 °F	ISO 1183
Melt Index of Compound	3.0 g/10 min @Load 2.16 kg, Temperature 190 °C	3.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	36	36	ASTM D2240
Tensile Strength at Break	12.0 MPa	1740 psi	ASTM D638
Elongation at Break	700 %	700 %	ASTM D638
Flexural Modulus	0.130 GPa	18.9 ksi	ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	95.0 °C	203 °F	DSC
Vicat Softening Point	65.0 °C @Load 0.999 kg	149 °F @Load 2.20 lb	ASTM D1525

Processing Properties	Metric	English	Comments
Processing Temperature	230 - 240 °C	446 - 464 °F	in case of extrusion coating with EVOH
	270 - 330 °C	518 - 626 °F

Descriptive Properties	Value	Comments
Ethyl Acrylate Content (%)	13	IRTF (internal)
Maleic Anhydride Content (%)	2.8	IRTF (internal)