Arkema Group LOTADER® 4503 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category Polymer , Adhesive , Thermoplastic , EMAAA Terpolymer
Manufacturer Arkema
Trade Name LOTADER®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group LOTADER® 4503 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LOTADER 4503 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized by high-pressure autoclave process.LOTADER 4503 is a versatile adhesive for extrusion lamination, designed as a ready for use resin to be used pure. LOTADER 4503 gives excellent adhesion to plain, primerless OPET films as well as to other plastic films like OPP, CPP and OPA. It also bonds to easier substrates like PE films, alu foil, metallized plastics, paper and board. Typical uses are:Adhesive for extrusion lamination of polar and non polar films and foils, particularly for laminates involving OPET and aluminium.Adhesive for coextrusion coating of LDPE / Tie / EVOH or PA / tie onto OPET or other films.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 0.940 g/cc

@Temperature 23.0 °C
0.0340 lb/in³

@Temperature 73.4 °F
ISO 1183
Methyl Acrylate Content 20 %
20 %
IRTF (internal)
Melt Index of Compound 8.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 25
25
ASTM D2240
Tensile Strength at Break 9.00 MPa
1310 psi
ASTM D638
Elongation at Break 750 %
750 %
ASTM D638
Flexural Modulus 0.0200 GPa
2.90 ksi
ASTM D638
Thermal Properties Metric English Comments
Melting Point 80.0 °C
176 °F
DSC
Vicat Softening Point 45.0 °C

@Load 0.999 kg
113 °F

@Load 2.20 lb
ASTM D1525
Processing Properties Metric English Comments
Processing Temperature <= 230 °C
<= 446 °F
for coextrusion with EVOH
270 - 330 °C
518 - 626 °F
Descriptive Properties Value Comments
Maleic Anhydride Content (%) 0.3
IRTF (internal)