Arkema Group Kynar® FLEX 2800 PVDF  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Kynar® FLEX 2800 PVDF  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 12086-VDF/HFP-K, EG1N, N. ?E7.D.G.B.C,, ? (3.5-7.5)Kynar FLEX PVDF are fluorinated thermoplastic copolymers.Outstanding characteristics of Kynar FLEX: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermomechanical properties.Main applications of Kynar FLEX: corrosion protection in the chemical industry, coating (painting, coextrusion), off shore, wire and cable.Kynar FLEX 2800 is a standard grade of granules which exhibits, compared to the homopolymer grades, a lower modulus, a better resistance to stress cracking in alkaline and oxidizing media, and a lower melting point.For cable coating, extrusion of tube and plaque, compression molding of bulky parts.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
Water Absorption 0.030 %
0.030 %
Moisture Absorption at Equilibrium 0.015 %
0.015 %
Humidity Absorption
Melt Flow 0.50 g/10 min

@Load 5.00 kg,
Temperature 230 °C
0.50 g/10 min

@Load 11.0 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 26.0 MPa
3770 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 12 %
12 %
50 mm/min
Tensile Modulus 0.700 GPa
102 ksi
1 mm/min
Charpy Impact, Notched 8.60 J/cm²
40.9 ft-lb/in²
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 160 µm/m-°C

@Temperature 20.0 °C
88.9 µin/in-°F

@Temperature 68.0 °F
Melting Point 142 °C
288 °F
10°C/min
Deflection Temperature at 0.46 MPa (66 psi) 68.0 °C
154 °F
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
Vicat Softening Point 79.0 °C
174 °F
50°C/hr; 50N
Glass Transition Temp, Tg -36.0 °C
-32.8 °F
10°C/min
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Oxygen Index 42 %
42 %
Electrical Properties Metric English Comments
Electrical Resistivity 2.00e+14 ohm-cm
2.00e+14 ohm-cm
Dielectric Constant 6.8

@Frequency 1e+6 Hz
6.8

@Frequency 1e+6 Hz
11

@Frequency 100 Hz
11

@Frequency 100 Hz
Dissipation Factor 0.052

@Frequency 100 Hz
0.052

@Frequency 100 Hz
0.233

@Frequency 1e+6 Hz
0.233

@Frequency 1e+6 Hz
Users viewing this material also viewed the following: