Arkema Group Cristamid® MS 1100 Semi-Aromatic Nylon (PASA) (Conditioned)

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Extrusion/Tubing Grade , Nylon, Aromatic
Manufacturer Arkema
Trade Name Cristamid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Cristamid® MS 1100 Semi-Aromatic Nylon (PASA) (Conditioned).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12/xx,MHLR,12-020Semi-aromatic polyamide (PASA) grade for injection molding and tubes extrusion.Transparency even thick. High resistance to environmental stress cracking. Good mechanical properties. Good thermal resistance. Dimensional stability.Example applications: Glasses.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa
10200 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 8.0 %
8.0 %
50 mm/min
Tensile Modulus 2.03 GPa
294 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB
NB
Low Temp
Charpy Impact, Notched 0.850 J/cm²
4.05 ft-lb/in²
1.24 J/cm²

@Temperature -30.0 °C
5.90 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature 20.0 °C
44.4 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Vicat Softening Point 115 °C
239 °F
50°C/hr; 50N
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Oxygen Index 26 %
26 %
Optical Properties Metric English Comments
Transmission, Visible 80 %
80 %
Mfr. reports 'Transparent' but doesn't quantify.
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
Dielectric Constant 3.4

@Frequency 100 Hz
3.4

@Frequency 100 Hz
Dielectric Strength 50.0 kV/mm
1270 kV/in
Dissipation Factor 0.020

@Frequency 100 Hz
0.020

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V