Aremco Ceramabond™ 835 High Temperature Ceramic Adhesive/Paste, Zirconia Filled

Category Ceramic , Oxide , Zirconium Oxide
Manufacturer Aremco
Trade Name Ceramabond™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aremco Ceramabond™ 835 High Temperature Ceramic Adhesive/Paste, Zirconia Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Fiber-Reinforced, Sets @ RT Bonding: Ceramic to Ceramic, Ceramic to Metal Principal Use: Halogen Lamps
Physical Properties Metric English Comments
Density 2.25 - 2.35 g/cc
0.0813 - 0.0849 lb/in³
Volatile Organic Compounds (VOC) Content 0.000 g/l
0.000 g/l
Viscosity 20000 - 40000 cP
20000 - 40000 cP
Mechanical Properties Metric English Comments
Impact Test 67.8 J
50.0 ft-lb
Torque Strength; curing at 1000°F
Thermal Properties Metric English Comments
CTE, linear 7.20 µm/m-°C
4.00 µin/in-°F
Maximum Service Temperature, Air 1650 °C
3000 °F
Electrical Properties Metric English Comments
Dielectric Strength 4.37 kV/mm
111 kV/in
Processing Properties Metric English Comments
Processing Temperature 50.0 - 90.0 °C
122 - 194 °F
Application Temp
Cure Time 120 min

@Temperature 93.3 °C
2.00 hour

@Temperature 200 °F
preceeded by <1 hour air set
Shelf Life 6.00 Month

@Temperature 4.44 - 32.2 °C
6.00 Month

@Temperature 40.0 - 90.0 °F
Descriptive Properties Value Comments
Acid Resistance Good
after curing at 700°F for 2 hours
Alkali Resistance Good
after curing at 700°F for 2 hours
Color Tan
Moisture Resistance Good
after curing at 700°F for 2 hours
Solvent Water
Thinner 835-T