Aremco Ceramabond™ 685-N High Temperature Ceramic Adhesive/Paste, Zirconia Filled

Category	Ceramic , Oxide , Zirconium Oxide
Manufacturer	Aremco
Trade Name	Ceramabond™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Aremco Ceramabond™ 685-N High Temperature Ceramic Adhesive/Paste, Zirconia Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: Bonds Plated Metals to Ceramic Bonding: Ceramic to Metal Principal Use: Heaters, Igniters, Gasketing

Physical Properties	Metric	English
Density	1.85 - 1.95 g/cc	0.0668 - 0.0704 lb/in³
Volatile Organic Compounds (VOC) Content	0.000 g/l	0.000 g/l
Viscosity	5000 - 20000 cP	5000 - 20000 cP

Mechanical Properties	Metric	English	Comments
Impact Test	47.5 J	35.0 ft-lb	Torque Strength; curing at 1000°F

Thermal Properties	Metric	English	Comments
CTE, linear	8.10 µm/m-°C	4.50 µin/in-°F
Maximum Service Temperature, Air	1650 °C	3000 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	6.93 kV/mm	176 kV/in

Processing Properties	Metric	English	Comments
Processing Temperature	50.0 - 90.0 °C	122 - 194 °F	Application Temp
Cure Time	120 min @Temperature 93.3 °C	2.00 hour @Temperature 200 °F	preceeded by 1-4 hour air set
Shelf Life	6.00 Month @Temperature 4.44 - 32.2 °C	6.00 Month @Temperature 40.0 - 90.0 °F

Descriptive Properties	Value	Comments
Acid Resistance	Good	after curing at 700°F for 2 hours
Alkali Resistance	Good	after curing at 700°F for 2 hours
Color	Tan
Moisture Resistance	Excellent	after curing at 700°F for 2 hours
Solvent	Water
Thinner	685-N-T