- Aremco Aremco-Bond™ 526N High Performance Epoxide
Aremco Aremco-Bond™ 526N High Performance Epoxide
| Category | Polymer , Adhesive , Thermoset , Epoxy |
| Manufacturer | Aremco |
| Trade Name | Aremco-Bond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Aremco-Bond™ 526N High Performance Epoxide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Clear-Amber, 1:1 System for Tough Bonding Applications Also available filled with aluminum oxide (Alumina) or pigments
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | |
| Viscosity | 8500 cP | 8500 cP | Mixed Viscosity |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 | 89 | |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Shear Strength | 19.3 MPa | 2800 psi | ASTM D1002-94 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 32.4 µm/m-°C @Temperature 20.0 °C |
18.0 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 300 °C | 572 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |
| Shrinkage | 1.0 % | 1.0 % | Cure Shrinkage |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+14 ohm-cm | 4.00e+14 ohm-cm | |
| Dielectric Constant | 3.01 @Frequency 1000 Hz |
3.01 @Frequency 1000 Hz |
|
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | |
| Dissipation Factor | 0.010 | 0.010 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 240 min | 4.00 hour | 2 hrs at 200°F; 2 hrs at 325°F (Recommended Cure) |
| 180 - 240 min @Temperature 149 °C |
3.00 - 4.00 hour @Temperature 300 °F |
Alternate Cure | |
| Pot Life | 150 min @Temperature 25.0 °C |
150 min @Temperature 77.0 °F |
100 gm mass |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Resistance | Good | |
| Color | Amber | |
| Mix Ratio By Weight | 1:1 | resin:hardener |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 88 FRD 1 Polypropylene Copolymer, Halogen Flame Retardant, UV Stabilized
- SABIC Innovative Plastics Lexan® FXE121R PC (Europe-Africa-Middle East)
- DSM Akulon® S223-TP4 (Dry) Impact Modified Nylon 66 (North America) (discontinued **)
- Mitsubishi Hostaphan® RN, 19 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- A. Schulman POLYBATCH™ Green 30394 Concentrate Based In LDPE
- Eagle Brass 102 OF COPPER (Non-Certified), Annealed
- BASF Ultraform N 2640 Z4 UNC Q600 POM
- 3M 8132LE Adhesive Transfer Tapes with Adhesive 300LSE
- ExxonMobil Santoprene® 191-55PA Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved